308/308L MIG
A5.9: ER308, ER308L
Used to weld Types 201, 302, 304 and 308 stainless steels. Can also be used for joining some dissimilar 300 series steels. Has a low carbon content to help prevent intergranular corrosion.
308/308L Sterling® AP
A5.4: E308-16 & E308L-16
Primarily designed for welding type 308L base metal with low or medium carbon content. Contains low carbon to avert carbide precipitation during welding as well as weld service. Excellent for weldin…
308/308L TIG
A5.9: ER308, ER308L
Used to weld Types 201, 302, 304 and 308 stainless steels. Can also be used for joining some dissimilar 300 series steels. Has a low carbon content to help prevent intergranular corrosion.
308L HiSil
A5.9: ER308LSi
A 308L chemistry which has been modified with a higher silicon level to increase weld puddle fluidity, ensuring better tie-ins and potentially higher welding speeds.
309/309L MIG
A5.9: ER309, ER309L
Used for joining similar 309L alloys or for joining 300-series stainless steels to carbon or low alloy steels.
309/309L Sterling® AP
A5.4: E309-16 & E309L-16
A lower carbon version of the 309(H) Sterling AP. Low carbon content makes it excellent for applications where reduced susceptibility to sensitization during high temperature service is necessary. O…
309/309L TIG
A5.9: ER309, ER309L
Used for joining similar 309L alloys or for joining 300-series stainless steels to carbon or low alloy steels.
309L HiSil
A5.9: ER309LSi
A modified 309L deposit. Higher silicon levels overcome the typical sluggish nature of 300-series stainless steel welding puddles.
310 Sterling® AP
A5.4: E310-16
Used to join 310 stainless as well as for the welding of steels with 20%-27% Chromium and 18%-22% Nickel. Used as a transition layer for high restrained joints of high carbon steels.
312 Sterling® AP
A5.4: E312-16
Designed for welding dissimilar joints of Type 312 metals. Can be used on hardenable steels, steel armor and generally hard-to-weld steels, offering outstanding performance with a directional arc and…
316/316L MIG
A5.9: ER316, ER316L
Formulated with molybdenum for increased pitting corrosion resistance and low carbon for better intergranular corrosion.
316/316L Sterling® AP
A5.4: E316-16 & E316L-16
Possesses properties similar to 316/316H Sterling AP except with a much lower carbon content which reduces susceptibility to sensitization during welding. The welds show high resistance to corrosion …
316/316L TIG
A5.9: ER316, ER316L
Formulated with molybdenum for increased pitting corrosion resistance and low carbon for better intergranular corrosion.
316L HiSil
A5.9: ER316LSi
Provides a 316L weld deposit but has better wetting action in the puddle due to higher levels of silicon.
Deckmaster™ 1139
E6022 (E4322*)
Designed for welding roof decking to support beams and other similar applications where burn-through spot welds with full penetration are required. Also designed to weld through galvanized or painted…
FabCO® 101
A5.29: E101T1-GM
This wire minimizes the crack sensitivity in quench and tempered low alloy steels such as ASTM A514. Excellent impact properties at low temperatures.
FabCO® 105D2
A5.29: E100T5-D2C
This product can be used for the repair of manganese-moly castings, or components that must undergo post weld heat treatment and maintain a tensile strength in the neighborhood of 100,000 psi. The bas…